High Frequency Nanocrystalline Strip For Transformer Iron Core Customized Size

  • 1
  • 2
  • 3

Brand Name : OHMALLOY

Model Number : 1k107

Certification : ROHS,ISO9001,UL /RoHs /SGS

Place of Origin : CHINA

MOQ : 100KG

Price : USD27/KG

Payment Terms : L/C, T/T,

Supply Ability : 10000KG/week

Delivery Time : 15WORKDAYS

Packaging Details : coil

Shape : Strip

Type : nanocrystalline ring core

Application : High-frequency boosting transformers,transformer

Composite : nanocrystalline strip

Material : nanocrystalline soft magnetic material

Size : customized

Color : Bright Silver

Contact Now

Application area:

  1. Switch power transformer and Pulse transformer iron core
  2. Power transformer , precision current mutual inductor iron core
  3. Leakage protection switch mutual inductor iron core
  4. Filtering inductance, storage inductance, the electric reactor iron core
  5. EMC common mode inductance and differential mode inductance iron core
  6. Saturable reactor, magnetic amplifier, Spike killer, Pulse Compressor iron core and magnetic bead


Features:

  1. High Saturation magnetic induction - reduce transformer volume
  2. High magnetic permeability low coercive force- improve transformer efficiency, mutual inductor sensitivity, reduce coil distribution parameters
  3. Low loss- reduce transformer temperature rise
  4. Good temperature stability - under 130ºC for long-term work
  5. Lower price - has the best cost performance of all the metal soft magnetic material




Typical Properties
Physical properties of Nanocrystalline alloy

Saturation magnetic induction (Bs) 1.25T Hardness (Hv) 880
Curie temperature (TC) 560ºC Density (d) 7.2g/cm3
Crystallizing temperature( Tx) 510ºC Resistivity(r) 90mW-cm
Saturation magnetostriction coefficient (ls) <2×10-6 Continuous operating temperature range -55-130ºC









Magnetic properties of Nanocrystalline alloy

Product Type Transverse magnetic annealing No magnetic annealing Longitudinal magnetic annealing
Initial permeability >2×104 >8×104 >1×104
Maximum permeability >5×104 >45×104 >50×104
Residual magnetic induction <0.2 T 0.6 T >0.85 T
Coercive force <1.8A/m <0.8A/m <1.8A/m
Iron loss P(20kHz, 0.5T) <30W/kg <50 W/kg <90W/kg
Iron loss P(100kHz, 0.3T) <150W/kg <150 W/kg <300W/kg
Iron loss rate(-55°C -125C ) <15% <15% <15%



The comparison between Nanocrystalline alloy and Permalloy iron alloy

Basic parameter Superfine crystal iron core Permalloy iron alloy (1J85) Ferrite
Saturation magnetic induction Bs(T) 1.25 0.75 0.5
Residual magnetic induction Br(T) 0.2~0.9 - 0.20
Saturation magnetostriction coefficient (×10-6) <2 <2 4
Resistivity (mmW-cm ) 80 56 106
Curie temperature /ºC 570 400 <200
Initial permeability μ0(Gs/Oe) >8×104 >8×104 -
Maximum permeability μm(Gs/Oe) >50×104 60×104 4×104
Coercive force Hc (A/m) <2 <1 6
Iron loss (20KHz,0.5T) (W/Kg) <35 - No
Iron loss (50KHz,0.3T) (W/Kg) <50 - No

Product Tags:

toroidal transformer core material

      

power transformer core material

      
Quality High Frequency Nanocrystalline Strip For Transformer Iron Core Customized Size for sale

High Frequency Nanocrystalline Strip For Transformer Iron Core Customized Size Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Ohmalloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)